氧化膜對于鋁板的質(zhì)量有很大的影響。氧化膜就是指鋁板在生產(chǎn)的過程中的厚度、孔隙率、透明度等。鋁板中膜層的厚度保持在10um以上就可以了，孔隙率以及透明度，這樣就可以得到比較好的染色質(zhì)量。
The oxide film has great influence on the quality of aluminum plate. Oxide film refers to the thickness, porosity and transparency of aluminum sheet in the process of production. Aluminum plate in the film thickness to maintain more than 10 um on it, porosity and transparency, so you can get better dyeing quality.
染色的溫度
Dyeing temperature
鋁板在染色的過程中分為冷染與熱染。使用冷染，所耗費的時間比較長，在染色的過程中期色彩的均勻性比較好掌握。熱染使用時間比較短，但是在染色的過程中對于顏色的操控比較難。熱染的溫度通常在10-60℃。如果在染色的過程中，溫度過高，會減小染色的吸附性，并且容易導(dǎo)致鋁板表面發(fā)花。
The aluminum plate is dyed in cold and heat. The use of cold dyeing, the time spent is longer, in the process of dyeing the color uniformity of the middle better grasp. The use of heat dyes is relatively short, but it is difficult to control the color in the dyeing process. The temperature of heat dyeing is usually 10-60 degrees. If the temperature is too high in the process of dyeing, it will reduce the adsorption of dyeing, and easily lead to the surface of aluminium plate flower.
鋁板制件原料的影響
Influence of raw materials on aluminum sheet
通常我們在生產(chǎn)的過程中高純鋁、鋁鎂、鋁錳合金經(jīng)過陽出彩氧化以后，其中染色的功能是較好的，可以染成各種各樣的顏色。對于含有硅或銅比較重的板材，在染色的過程中只能夠染成深色與黑色，比較單調(diào)的顏色。
Usually we in the production process of high-purity aluminum, aluminum magnesium, aluminum manganese alloy after anodizing, of which the function of dyeing is the best, can be dyed into a variety of colors. For heavy plates containing silicon or copper, the dyeing process can only be dyed dark and black, relatively monotonous color.
染色液濃度

Dyeing solution concentration
鋁板的濃度與染色之間存在一定的聯(lián)系，如果鋁板染成淡色，其中濃度可以降低一點，染成深色濃度可以高一點。
There is a certain relationship between the concentration of aluminum plate and dyeing, if the aluminum plate dyed light, the concentration can be reduced a little, dyed dark concentration can be higher.
通常所生產(chǎn)的鋁板材料所染比較淡的顏色其色彩為0.1-0.39g/L，染淡色彩為1g/L，染深色彩為3-5g/L，染稠密的色彩為10-15g/L，如果要求的染色濃度比較高就會造成顏色不均或者會出現(xiàn)浮色的現(xiàn)象，在清潔與關(guān)閉的過程匯總?cè)菀桩a(chǎn)生流色。
Usually the lighter colors of the aluminum sheet materials are 0.1-0.39g/L, 1g/L, 3-5g/L, and 10-15g/L. If the required dyeing concentration is high, the color will be uneven or float, and flow will easily occur during the cleaning and closing process. Color.
為了加強其染色的吸附性能，這樣可以使用低濃度顏色進行延伸染色，這樣可以使染料能夠比較均勻的滲透到氧化膜中，這樣可以使染色更加和諧與牢固。
In order to enhance its dyeing adsorption performance, this can use low concentration of color for extended dyeing, so that the dye can be more uniform penetration into the oxide film, this can make the dyeing more harmonious and firm.